Black ceramic pigments for porcelain tile bodies produced with chromite ores and iron oxide waste

TANIŞAN B., TURAN S.

JOURNAL OF CERAMIC PROCESSING RESEARCH, cilt.12, sa.4, ss.462-467, 2011 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 12 Sayı: 4
  • Basım Tarihi: 2011
  • Dergi Adı: JOURNAL OF CERAMIC PROCESSING RESEARCH
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.462-467
  • Eskişehir Osmangazi Üniversitesi Adresli: Evet

Özet

In this study, two different natural chromite ores and iron oxide waste from the steel rolling industry were used as less expensive alternative raw materials for the synthesis of black ceramic pigments to be used in porcelain tile bodies. The effects of chromite ore-iron oxide waste ratios and calcination temperature on the pigment properties were investigated. It was found that chromite ore with a higher Cr2O3/FeO ratio can be used to synthesise black ceramic pigments when combined with the iron oxide waste. However, their color intensity was not as strong as commercial black pigments due to the presence of other phases and impurities coming from the chromite ores. When these pigments were used in combination with commercial black pigments, the consumption of the commercial pigments can be reduced, providing cost savings for coloration of porcelain tile bodies.