Ultra-conductive wires with cascaded carbon nanotube/Cu structure


Ozmen A., Mobtakeri S., Kocak Y., Akbaba U., ERTUĞRUL M., GÜR E.

DIAMOND AND RELATED MATERIALS, cilt.120, 2021 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 120
  • Basım Tarihi: 2021
  • Doi Numarası: 10.1016/j.diamond.2021.108711
  • Dergi Adı: DIAMOND AND RELATED MATERIALS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Academic Search Premier, PASCAL, Aerospace Database, Chemical Abstracts Core, Communication Abstracts, INSPEC, Metadex, Civil Engineering Abstracts
  • Anahtar Kelimeler: Ultra-conductive wire, Carbon nanotubes, Cu wire, Inverted cylindrical magnetron sputtering, HIGH AMPACITY, COMPOSITE
  • Eskişehir Osmangazi Üniversitesi Adresli: Hayır

Özet

In the present study, ultra-conductive wires were produced by the cascaded Cu/MWCNT wire structure. Cascaded wires were prepared on the industrial 1 mm diameter Cu wire with two steps; Firstly, electrophoretic deposition (EPD) was used to deposit the functionalized MWCNT on the Cu wires. Secondly, a novel inverted cylindrical magnetron sputtering (ICMS) has been built to coat Cu on the MWCNT deposited Cu wire. Different number of cascaded layers up to 13 layers of Cu/MWCNT wires as well as different Cu coating parameter were produced. High deposition rate of MWCNT on Cu wires has been achieved by the EPD method. As can be seen from the cross-sectional SEM images, the intended cascaded structures were successfully formed. The ampacity of the 1 mm industrial Cu wire used in this study has increased by 9.2%. In addition, the temperature of the cascaded wires has shown slow increase compared to that of reference Cu wire. On the other hand, the maximum current able to carry with 1 degrees C temperature raise has increased by 50%.