Comparisons of surface and optical properties of the heavily carbon-doped GaN nanocrystalline films deposited by thermionic vacuum arc method


PAT S., Ozen S., ŞENAY V., KORKMAZ Ş.

VACUUM, cilt.133, ss.38-42, 2016 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 133
  • Basım Tarihi: 2016
  • Doi Numarası: 10.1016/j.vacuum.2016.08.013
  • Dergi Adı: VACUUM
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.38-42
  • Eskişehir Osmangazi Üniversitesi Adresli: Evet

Özet

In this paper, heavily C-doped GaN samples were deposited on glass and PET substrates by the therm ionic vacuum arc (TVA) method, for the first time. Microstructure, surface and optical properties of the carbon-doped GaN samples were investigated by X-ray diffraction (XRD), field emission scanning electron microscopy, atomic force microscopy, and UV-Vis spectrophotometer. According to XRD pattern, fullerene (C-60) structures were able to deposit in doped samples, for the first time. The fullerene structures were detected at heavily carbon-doped GaN. The obtained band gap changes of heavily carbon-doped GaN samples are determined. The band gap of CGaN on PET substrate decreased to a lower value, about 100 meV. The band gaps were shifted to the lowest wavelengths towards the edge of the UV region by heavily doped carbon. (002) and (004) peaks for GaN were also detected. (C) 2016 Elsevier Ltd. All rights reserved.