JOURNAL OF MATERIALS CHEMISTRY C, cilt.5, sa.9, ss.2368-2379, 2017 (SCI-Expanded)
The design and development of novel ambipolar semiconductors is very crucial to advance various optoelectronic technologies including organic complementary (CMOS) integrated circuits. Although numerous high-performance ambipolar polymers have been realized to date, small molecules have been unable to provide high ambipolar performance in combination with ambient-stability and solution-processibility. In this study, by implementing highly p-electron deficient, ladder-type IFDK/IFDM acceptor cores with bithiophene donor units in D-A-D pi-architectures, two novel small molecules, 2OD-TTIFDK and 2OD-TTIFDM, were designed, synthesized and characterized in order to achieve ultralow band-gap (1.21-1.65 eV) semiconductors with sufficiently balanced molecular energetics for ambipolarity. The HOMO/LUMO energies of the new semiconductors are found to be -5.47/-3.61 and -5.49/-4.23 eV, respectively. Bottom-gate/top-contact OFETs fabricated via solution-shearing of 2OD-TTIFDM yield perfectly ambient stable ambipolar devices with reasonably balanced electron and hole mobilities of 0.13 cm(2) V-1 s(-1) and 0.01 cm(2) V-1 s(-1), respectively with I-on/I-off ratios of similar to 10(3)-10(4), and 2OD-TTIFDK-based OFETs exhibit ambipolarity under vacuum with highly balanced (mu(e)/mu(h) similar to 2) electron and hole mobilities of 0.02 cm(2) V-1 s(-1) and 0.01 cm(2) V-1 s(-1), respectively with I-on/I-off ratios of similar to 10(5)-10(6). Furthermore, complementary-like inverter circuits were demonstrated with the current ambipolar semiconductors resulting in high voltage gains of up to 80. Our findings clearly indicate that ambient-stability of ambipolar semiconductors is a function of molecular orbital energetics without being directly related to a bulk p-backbone structure. To the best of our knowledge, considering the processing, charge-transport and inverter characteristics, the current semiconductors stand out among the best performing ambipolar small molecules in the OFET and CMOS-like circuit literature. Our results provide an efficient approach in designing ultralow band-gap ambipolar small molecules with good solution-processibility and ambient-stability for various optoelectronic technologies, including CMOS-like integrated circuits.