A novel thermoresponsive hydrogel matrix based on poly(N-ethoxypropylacrylamide)


Solener M., Uguzdogan E., Nurbas M., Camli T., Kabasakal O. S., Patir S., ...Daha Fazla

POLYMER BULLETIN, cilt.57, sa.3, ss.341-349, 2006 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 57 Sayı: 3
  • Basım Tarihi: 2006
  • Doi Numarası: 10.1007/s00289-006-0570-y
  • Dergi Adı: POLYMER BULLETIN
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.341-349
  • Eskişehir Osmangazi Üniversitesi Adresli: Evet

Özet

A new temperature sensitive hydrogel matrix, poly(N-ethoxypropylacrylamide), PNEPAM, was obtained by the bulk polymerization of N-ethoxypropylacrylamide (NEPAM). The monomer, NEPAM was synthesized by the nucleophilic substitution reaction of 3-ethoxypropylamine and acryloyl chloride. The polymerization was performed at +4 degrees C, by using N,N-methylenebisacrylamide (MBAM) as crosslinker, polyethyleneglycol (PEG) 4000 as diluent, and potassium persulfate (KPS) and tetramethylethylenediamine (TEMED) as the initiator and accelerator, respectively. PNEPAM gel matrices exhibited a thermosensitive bahaviour reasonably similar to poly(N-isopropylacrylamide), PNIPAM gels. The equilibrium swelling ratio at constant temperature increased with increasing initiator concentration and decreasing monomer concentration. The use of PEG 4000 as a diluent in the gel synthesis resulted in a significant enhacement in the thermosensitivity of gel matrix. The equilibrium swelling ratios up to 60 g water/g dry gel were observed in the low-temperature region. The results indicated that PNEPAM gel is a new alternative thermosensitive material to the NIPAM based gels.