2006 TMS Fall Extraction and Processing Division: Sohn International Symposium, San Diego, CA, Amerika Birleşik Devletleri, 27 - 31 Ağustos 2006, cilt.6, ss.605-612
In this study the effects of interstitial ratios on k-feldspar samples were investigated. The k-feldspar samples were taken from Egypt using dry batch grinding conditions and a kinetic model. Three different mono size fractions (-3350+2360, -850+600 and -300+212 μm) were ground separately for 0.5, 1, 4, and 8 minutes and at four different interstitial ratios (125%, 100%, 75% and 50%) using a Bond mill with a mixture of five ball sizes. The mill used was at a size of 30.5 cm diameters, with 30.5 cm length, providing a total mill volume of 22272 cm3. The mill has a total mass consisting of 22648 g. steel ball mixtures of 38.10, 31.75, 25.40, 19.05 and 12.70mm diameters, occupying 22% of mill volume. The mill rotates at a speed of 70 rpm. The weights of the feed charges were 3000, 2000, 1000, and 500 g for 125%, 100%, 75% and 50% filling of the interstices of the balls respectively. The specific rate of breakage (S i) was determined from the top size fractions at different grinding times that were mentioned above and the model parameters were compared for the four different powder filling ratios (U). In many investigations, it has been found that an interstitial filling ratio of U = 0.6-1.1 is a good powder ball loading ratio to give an efficient breakage in a ball mill. In this study, it was found that U=1.25 is a good ratio for K-Feldspar.